[iMiD 2017] LG Display, Spur Development of 77 inch transparent flexible OLED

/0 코멘트/카테고리: /작성자:

LG Display’s Kwon Se-Yeol senior researcher introduced the 77-inch transparent flexible OLED which had been introduced in June at IMID 2017 held in BEXCO, Busan on Aug. 30, and announced the applied technologies to realize this.

 

 

Kwon Se-Yeol senior researcher mentioned, “OLED is self-luminous, so it can be manufactured with a thin thickness because it does not need a back light unit. The thinner the thickness, the more flexible the OLED can be so that it is easy to implement flexible displays with OLEDs.” and forecasted. “It can be used in various fields such as signage and smart desk.”

 

 

The 77-inch transparent flexible OLED which is released this time is a top emission type for improved luminance. The transparent thin film encapsulation layer is applied, different from the conventional OLED TV or large flexible OLED, and two polyimide substrates are used.

 

Kwon Se-Yeol senior researcher said “We applied a transparent thin-film encapsulation layer instead of the existing metal encapsulation layer for the top emission method ” and explained “A white OLED light emitting layer and a color filter layer were formed on two polyimide substrates and cemented together. A barrier film and a multi-barrier were applied to the top and bottom of the polyimide substrates to prevent moisture and oxygen penetration.”

 

 

The Kwon Se-Yeol senior researcher then states that “flexural rigidity of the panel is mainly affected by the thickness of the polarizer and the encapsulant layer, so it is necessary to reduce the thickness in order to improve the flexibility”, and emphasized “By reducing the thickness of the encapsulant layer from 100 μm to 20 μm, we can reduce the strain on the OLED module from 0.36% to 0.21%, along with improved flexibility”.

In addition, he mentioned that surface reflection due to polyimide birefringence phenomenon, laser wavelength selection according to polyimide properties in LLO (laser lift off) process, and use of flexible OLED module are all covered, and technical development is continuing.

Meanwhile, LG Display has developed the world’s first 77-inch transparent flexible OLED with UHD (3840 × 2160) resolution, transmittance of 40%, and radius of curvature of 80R as part of the national project.

[iMiD 2017] LG Display, 77 inch 투명 플렉시블 OLED 개발 박차

/0 코멘트/카테고리: , , , /작성자:

LG Display의 권세열 책임은 8월 30일 부산 벡스코에서 개최중인 IMID 2017에서 지난 6월 선보인 77 inch 투명 플렉시블 OLED를 소개하며 이를 구현하기 위해 적용 된 기술들을 발표하였다.

 

 

권세열 책임은 “OLED는 자발광이라 back light unit이 필요 없어 얇은 두께로 제작이 가능하며, 두께가 얇을 수록 유연성이 향상 되기 때문에 OLED는 플렉시블 디스플레이를 구현하기 용이하다”고 언급하며 “추후 사이니지와 스마트 책상 등 여러 분야에서 적용이 될 수 있을 것”이라 전망했다.

 

 

 

이번에 공개 된 77 inch 투명 플렉시블 OLED는 휘도 향상을 위한 전면 발광방식으로, 기존의 OLED TV나 대형 플렉시블 OLED와는 다르게 투명박막 봉지층이 적용되었으며 polyimide 기판이 2장 사용 되었다.

권세열 책임은 “전면 발광방식을 위해 기존의 금속 봉지층 대신 투명 박막 봉지층을 적용하였다”고 밝히며 “2장의 polyimide 기판에 각각 white OLED 발광층과 칼라필터층을 형성하여 합착 하였다. polyimide 기판 상하부에는 수분과 산소 침투를 방지하기 위해 barrier film과 multi barrier가 적용 되었다”라고 설명했다.

 

이어서 권세열 책임은 “패널의 휨 강성(flexural rigidity)는 주로 편광판과 봉지층 두께의 영향을 받기 때문에 유연성을 향상시키기 위해서는 두께를 줄이는 것이 필수”라며 “봉지층의 두께를 100um에서 20um까지 줄이면 유연성 향상과 함께 OLED 모듈에 가해지는 변형율(strain)도 0.36%에서 0.21%까지 저감할 수 있을 것”이라 강조하였다.

그 밖에 polyimide 복굴절 현상으로 인한 표면반사이슈와 LLO(laser lift off) 공정 시 polyimide 성질에 따른 laser의 파장 선택, 유연성을 가지는 OLED 모듈 사용 등의 주요 이슈를 다루며 기술 개발이 지속적으로 이루어지고 있다고 언급했다.

한편, LG Display는 국책과제의 일환으로써 UHD(3840 × 2160) 해상도와 투과율 40%, 곡률반경 80R을 가지는 77 inch 투명 플렉시블 OLED를 세계 최초로 개발한 바 있다.